Noryl PPO PX1005X物性
PPE+PS合金,无溴无氯阻燃,UL94 V0/5VA .优异的介电强度,用于电子/电气市场的室内/室外应用。|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
560
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
420
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
3.1
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
17
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
24400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
810
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
810
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus
|
24700
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
22400
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
53
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
43
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
2.8
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
12.5
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2460
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
76
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2480
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, unnotched, 23°C
|
119
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
30
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
9
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
22
|
kJ/m2
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
23
|
kJ/m2
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
107
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
84
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
72
|
°C
|
ASTM D 648
|
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
88
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
78
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
8.9E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
1.03E-04
|
1/°C
|
ASTM E 831
|
|
|
Vicat Softening Temp, Rate B/50
|
94
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
97
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
88
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
75
|
°C
|
ISO 75/Ae
|
|
|
Relative Temp Index, Elec
|
95
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
80
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
95
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.12
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Mold Shrinkage on Tensile Bar, xflow (2)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 280°C/5.0 kgf
|
37
|
g/10 min
|
ASTM D 1238
|
|
|
Melt Volume Rate, MVR at 280°C/5.0 kg
|
37
|
cm3/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Volume Resistivity
|
3.3E+16
|
Ohm-cm
|
ASTM D 257
|
|
|
Surface Resistivity
|
>1.E+16
|
Ohm
|
ASTM D 257
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17.7
|
kV/mm
|
ASTM D 149
|
|
|
Relative Permittivity, 50/60 Hz
|
2.67
|
-
|
ASTM D 150
|
|
|
Relative Permittivity, 1 MHz
|
2.53
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 50/60 Hz
|
0.012
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 1 MHz
|
0.0026
|
-
|
ASTM D 150
|
|
|
Arc Resistance, Tungsten {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.01
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VA Rating (3)
|
2.99
|
mm
|
UL 94
|
|
|
UV-light, water exposure/immersion
|
F1
|
-
|
UL 746C
|
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
75 - 80
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
250 - 275
|
°C
|
|
Nozzle Temperature
|
250 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
240 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
225 - 270
|
°C
|
|
Rear - Zone 1 Temperature
|
215 - 265
|
°C
|
|
Mold Temperature
|
55 - 75
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
20 - 100
|
rpm
|
|
Shot to Cylinder Size
|
30 - 70
|
%
|
|
Vent Depth
|
0.038 - 0.051
|
mm
|
供应：PPO EXT115 EXT130 高流动性，耐油性已改进适合汽车工业零件
供应：PPO HMC3008 导电性专用级，UL94V-1
供应：PPO HS2000 复合增强级，低翘曲，含20%填充料，UL94V-0
供应：PPO NC120/NC208 NC212/NC112 NC108/NC220 导电性专用级，UL94V-1
供应：PPO NF1020 滑动性专用级，含填充料，UL94HB
供应：PPO NFV1030 滑动性专用级，含填充料，UL94HB
供应：PPO PX2611 PX2622 高流动性，适合汽车工业部件
供应：PPO PX2728 通用级，热变形温度80-98℃，UL94V-1
供应：PPO PX2801/ SE225 通用级，热变形温度100-119℃，UL94V-1
供应：PPO SE1-GN1 注塑增强级，含10%玻纤，UL94V-1
供应：PPO SE1-GN2 注塑增强级，含20%玻纤，UL94V-1
供应：PPO SFG100/200/300 泡沫级，含填充材料改性，UL94V-0,适合阻燃制品
供应：PPO TN15/STN20 高抗冲击级，适合汽车工业部件
供应：PPO BHM510 阻燃注塑级。高弹性，UL94V-0，热变形温度110℃。机械、电器、电子等阻燃的工程结构部件
供应：PPO CRN-520 注塑级，耐热、耐化学性能，用于机械、化工部件及防腐蚀制品
供应：PPO CRN-530 注塑级，特点和用途同CRN-520
供应：PPO CRN-720/730 注塑级，特点和用途同CRN-520
供应：PPO DSN-300I/400I /500I 注塑级，用于导电、电磁波屏蔽
供应：PPO EN212 挤塑级，UL94V-1,相对密度110。适合电器、电子、化工、机械等结构部件
供应：PPO EN265 挤塑级，UL94V-1,相对密度107。适合电器、电子、化工、机械等结构部件
供应：PPO ENG265 挤塑级，UL94HB,相对密度106。适合电器、电子、化工、机械等结构部件
供应：PPO FN150 发泡级，用于特殊需要的发泡工程制品
供应：PPO FN215 发泡级，相对密度080。适合特殊需要的发泡工程制品
供应：PPO FM-3020 发泡级，用于特殊需要的发泡工程制品
供应：PPO GFN1 增强注塑级。10%玻纤，热变形温度120℃，UL94HB,UL认可电器长期使用温度90℃，相对密度114。适合电器、电子、机械等结构工程部件
供应：PPO GFN2 增强注塑级。20%玻纤，热变形温度140℃，相对密度121。其他特点用途同GFN1
供应：PPO GFN3 增强注塑级。30%玻纤，热变形温度142℃，UL94HB,相对密度127。其他特点用途同GFN1
供应：PPO GTX-600/910 注塑级，PPO/PA合金
供应：PPO HGF-100 注塑阻燃级，UL94V-0,高弹性，外观，机械性能优，适合电器、电子、机械等工业部件，阻燃制品
供应：PPO HFG-200/300 注塑阻燃级，特点和用途同HGF-100
供应：PPO HM3020 复合增强级。高刚性，HDT 120℃，UL94V-0,相对密度131。适合电器电子、机械等结构工程制品
供应：PPO HM4025 复合增强级。高刚性，HDT 125℃，UL94V-0。适合电器电子、机械等结构工程制品
供应：PPO N85 阻燃注塑级，UL94V-0, HDT 85℃。适合电器、电子、机械。化工等。如屏蔽套、壳体箱、机架
供应：PPO N90 阻燃注塑级，UL94V-0, HDT 90℃。适合电器、电子、机械。化工等。如屏蔽套、壳体箱、机架
供应：PPO N190 阻燃注塑级。热变形温度90℃，UL94V-0,UL认可电器长期使用温度95℃，相对密度108。适合阻燃和大型外装用的电器、电子等工程制品
1222/2615 注塑级，增强型，高强度，汽车专用级
供应：PPO PX-2725 阻燃注塑级，热变形温度105℃，UL94V-1,适合阻燃和耐热的电器、电子、化工、机械等结构制品
供应：PPO PX-2890 注塑级，增强型，用于电子电器、机械、化工零件及工程部件
供应：PPO PX-2891 注塑级，特点和用途同PX-2890
供应：PPO PX-2922 注塑级，20%玻纤增强，UL94V-0，用于电子电器、机械、工业零部件及阻燃工程制品
供应：PPO PX-2923 注塑级，30%玻纤增强，其他特点和用途同PX-2922
供应：PPO PX-2925 注塑级，增强型，用于电器、电子、机械、汽车工业部件
供应：PPO PX-2926 复合增强级。热变形温度110℃，高刚性，UL94V-0，用于电子电器、机械等阻燃工程制品
供应：PPO PX-2930 注塑增强级，UL94V-0，用于电子电器、机械、汽车工业部件及阻燃工程制品
供应：PPO PX9406 注塑级。适合电视机外壳专用料
供应：PPO PX9406 注塑级。非增强，UL94V-0，热变形温度125℃，UL认可长期使用温度105℃，相对密度109。适合要求阻燃和耐热的电器、电子、化工、机械等结构工程制品
另有其他原料牌号无法详细介绍，具体事宜（物性、报价、UL报告、RoSH标准、SGS检测报告等）敬请来函来电联系！本公司还长期供应PA/ABS、PP、PA6、PA66、PBT、PEI、PET、PMMA、POM、PPS等公司货源充足，品种齐全，价格合理。