| 详细介绍： PA66 G/25-V0KB1 NAT0046 熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。熔化温度应避免高于300℃。 模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。
|
物性表：
|
|
Physical Properties
|
Metric
|
English
|
Comments
|
|
Density
|
1.35 g/cc
|
0.0488 lb/in3
|
ISO 1183
|
|
|
|
Mechanical Properties
|
Metric
|
English
|
Comments
|
|
Tensile Strength at Break
|
145 MPa
|
21000 psi
|
ISO 527
|
|
Elongation at Break
|
2.4 %
|
2.4 %
|
ISO 527
|
|
Flexural Modulus
|
7.90 GPa
|
1150 ksi
|
ISO 178
|
|
Izod Impact, Notched (ISO)
|
7.70 kJ/m2
|
3.66 ft-lb/in2
|
ISO 180
|
|
Charpy Impact, Notched
|
0.850 J/cm2
|
4.04 ft-lb/in2
|
ISO 179
|
|
|
|
Thermal Properties
|
Metric
|
English
|
Comments
|
|
Deflection Temperature at 1.8 MPa (264 psi)
|
245 °C
|
473 °F
|
ISO 75
|
|
|
|
Processing Properties
|
Metric
|
English
|
Comments
|
|
Melt Temperature
|
285 - 300 °C
|
545 - 572 °F
|
|
|
Mold Temperature
|
80.0 - 90.0 °C
|
176 - 194 °F
|
|
|
Dry Time
|
2 - 4 hour
|
2 - 4 hour
|
|
|
Moisture Content
|
<= 0.050 %
|
<= 0.050 %
|
|
|
|
|
Descrtptive Properties
|
|
Color
|
NAT 0046
|
|
|
Commercial Status
|
North America
|
性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。 |