PA66 AZ HP UV BK23220产品展示-PA66 AZ HP UV BK23220资料-PA66 AZ HP UV BK23220招商信息-

　　 PA66 AK8 PA66 AFR450B 物理化学性：PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

Physical Properties	Metric	English	Comments
物性表：
Density	1.55 g/cc	0.0560 lb/in3	ISO 1183
Water Absorption at Saturation	4.5 % @Temperature 23.0 °C	4.5 % @Temperature 73.4 °F	ISO 62-1
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	on Tensile Bar; E2P method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	120 MPa	17400 psi	5 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	5 mm/min; ISO 527
Tensile Modulus	9.20 GPa	1330 ksi	1 mm/min; ISO 527
Flexural Strength	175 MPa	25400 psi	break, 2 mm/min; ISO 178
Flexural Modulus	8.90 GPa	1290 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m2 @Temperature -20.0 °C	2.86 ft-lb/in2 @Temperature -4.00 °F	80x10x4; ISO 180/1A
	7.00 kJ/m2 @Temperature 23.0 °C	3.33 ft-lb/in2 @Temperature 73.4 °F	80x10x4; ISO 180/1A
Charpy Impact Unnotched	5.50 J/cm2	26.2 ft-lb/in2	Edgew 80x10x4 sp=62; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	27.0 μm/m-°C @Temperature 23.0 - 60.0 °C	15.0 μin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	92.0 μm/m-°C @Temperature 23.0 - 60.0 °C	51.1 μin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	256 °C	493 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point	258 °C	496 °F	B/120; ISO 306
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in

Processing Properties	Metric	English	Comments
Zone 1	260 - 270 °C	500 - 518 °F
Zone 2	270 - 280 °C	518 - 536 °F
Zone 3	270 - 285 °C	518 - 545 °F
Melt Temperature	270 - 285 °C	518 - 545 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	75.0 - 85.0 °C @Time 14400 - 21600 sec	167 - 185 °F @Time 4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %