| 详细介绍：
EMERGE PC 4903
Advanced Resin
30% 玻璃纤维增强材料
Trinseo
产品说明:
EMERGE PC 4903 is a 30% glass fiber reinforced high flow ignition resistant polycarbonate resin. This resin does not contain bromine and chlorine flame retardants. EMERGE PC 4903 is designed with superior processability for use in structural parts of printers, scanners, copiers as well as internal parts for ITE applications.
Applications:
· Structural parts of printers, scanners, and copiers
· Internal parts of ITE machines
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
1.46
|
g/cm³
|
ASTM D792
|
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
12
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动
|
0.20 到 0.40
|
%
|
ASTM D955
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
6800
|
MPa
|
ASTM D638
|
|
抗张强度 (屈服, 3.20 mm, 注塑)
|
116
|
MPa
|
ASTM D638
|
|
弯曲模量 (3.20 mm, 注塑)
|
8400
|
MPa
|
ASTM D790
|
|
弯曲强度 (3.20 mm, 注塑)
|
155
|
MPa
|
ASTM D790
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C, 3.20 mm, 注塑)
|
130
|
J/m
|
ASTM D256
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火)
|
100
|
°C
|
ASTM D648
|
|
可燃性
|
额定值
|
|
测试方法
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
1.00 mm 3
|
V-0
|
|
|
|
2.00 mm
|
5VA
|
|
|
|
注射
|
额定值
|
单位制
|
|
|
干燥温度
|
110
|
°C
|
|
|
干燥时间
|
6.0 到 8.0
|
hr
|
|
|
料筒后部温度
|
250 到 260
|
°C
|
|
|
料筒中部温度
|
260 到 270
|
°C
|
|
|
料筒前部温度
|
260 到 280
|
°C
|
|
|
射嘴温度
|
271 到 300
|
°C
|
|
|
模具温度
|
60.0 到 100
|
°C
|
|
EMERGE PC 4903
EMERGE PC 4903