INLUBE PCGF30TF15
聚碳酸酯
30% 玻璃纤维增强材料
Infinity LTL Engineered Compounds
产品说明:
· Inlube PTFE, silicone, MoS2 and graphite internally lubricated compounds
· Offered in all Infinity base resins and can be combined with reinforcements and process additives
· Provide reduced coefficient of friction and low wear, including enhanced mechanical and thermal propertie
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
1.55
|
g/cm³
|
ASTM D792
|
|
特定体积
|
0.646
|
cm³/g
|
|
|
收缩率 - 流动
|
0.10 到 0.20
|
%
|
ASTM D955
|
|
吸水率 (24 hr)
|
0.060
|
%
|
ASTM D570
|
|
硬度
|
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (M 级)
|
95
|
|
ASTM D785
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
抗张强度 (屈服)
|
121
|
MPa
|
ASTM D638
|
|
伸长率 (屈服)
|
2.0 到 4.0
|
%
|
ASTM D638
|
|
弯曲模量
|
8270
|
MPa
|
ASTM D790
|
|
弯曲强度
|
179
|
MPa
|
ASTM D790
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (3.18 mm)
|
170
|
J/m
|
ASTM D256
|
|
无缺口悬臂梁冲击 (3.18 mm)
|
640
|
J/m
|
ASTM D256
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火)
|
149
|
°C
|
ASTM D648
|
|
线形热膨胀系数 - 流动
|
2.7E-5
|
cm/cm/°C
|
ASTM D696
|
|
电气性能
|
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+16
|
ohms
|
ASTM D257
|
|
可燃性
|
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.59 mm)
|
HB
|
|
UL 94
|
|
注射
|
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
加工（熔体）温度
|
282 到 332
|
°C
|
|
|
模具温度
|
93.3
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.038 到 0.076
|
mm
|
|
INLUBE PC PCGF30TF15
INLUBE PC PCGF30TF15