| 详细介绍：
LNP LUBRICOMP DFL36 compound
聚碳酸酯
30% 玻璃纤维增强材料
SABIC Innovative Plastics
产品说明:
LNP LUBRICOMP DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Also known as: LNP LUBRICOMP Compound DFL-4036
Product reorder name: DFL36
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
1.54
|
g/cm³
|
ASTM D792
|
|
收缩率 - 横向流动 (24小时)
|
0.50
|
%
|
ASTM D955
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|
|
|
|
-- 2
|
9580
|
MPa
|
ASTM D638
|
|
--
|
9080
|
MPa
|
ISO 527-2/1
|
|
抗张强度
|
|
|
|
|
屈服
|
123
|
MPa
|
ASTM D638
|
|
屈服
|
118
|
MPa
|
ISO 527-2
|
|
断裂
|
123
|
MPa
|
ASTM D638
|
|
断裂
|
118
|
MPa
|
ISO 527-2
|
|
伸长率
|
|
|
|
|
屈服
|
2.6
|
%
|
ASTM D638, ISO 527-2
|
|
断裂
|
2.8
|
%
|
ASTM D638
|
|
断裂
|
2.7
|
%
|
ISO 527-2
|
|
弯曲模量
|
|
|
|
|
--
|
8620
|
MPa
|
ASTM D790
|
|
--
|
8340
|
MPa
|
ISO 178
|
|
弯曲强度
|
|
|
|
|
--
|
186
|
MPa
|
ASTM D790
|
|
--
|
185
|
MPa
|
ISO 178
|
|
摩擦系数
|
|
|
ASTM D3702 Modified
|
|
Dynamic
|
0.46
|
|
|
|
Static
|
0.41
|
|
|
|
磨损因数 - Washer
|
22.0
|
10^-10 in^5-min/ft-lb-hr
|
ASTM D3702 Modified
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
23°C
|
200
|
J/m
|
ASTM D256
|
|
23°C 3
|
19
|
kJ/m²
|
ISO 180/1A
|
|
无缺口悬臂梁冲击
|
|
|
|
|
23°C
|
920
|
J/m
|
ASTM D4812
|
|
23°C 3
|
55
|
kJ/m²
|
ISO 180/1U
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火, 3.20 mm)
|
144
|
°C
|
ASTM D648
|
|
注射
|
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料筒后部温度
|
293 到 304
|
°C
|
|
|
料筒中部温度
|
310 到 321
|
°C
|
|
|
料筒前部温度
|
321 到 332
|
°C
|
|
|
加工（熔体）温度
|
304 到 327
|
°C
|
|
|
模具温度
|
82.2 到 110
|
°C
|
|
|
背压
|
0.172 到 0.344
|
MPa
|
|
|
螺杆转速
|
30 到 60
|
rpm
|
|
LUBRICOMP PC DFL36
LUBRICOMP PC DFL36