TYPICAL PROPERTIES ⁽¹⁾

MECHANICAL

value

Unit

Standard

Tensile Stress, yld, Type I, 50 mm/min

77

MPa

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

70

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

6

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

80

%

ASTM D 638

Tensile Modulus, 5 mm/min

2600

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

115

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

2500

MPa

ASTM D 790

Tensile Stress, yield, 50 mm/min

77

MPa

ISO 527

Tensile Stress, break, 50 mm/min

70

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

6

%

ISO 527

Tensile Strain, break, 50 mm/min

80

%

ISO 527

Tensile Modulus, 1 mm/min

2600

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

110

MPa

ISO 178

Flexural Modulus, 2 mm/min

2700

MPa

ISO 178

IMPACT

value

Unit

Standard

Izod Impact, notched, 23°C

130

J/m

ASTM D 256

Izod Impact, notched, -30°C

90

J/m

ASTM D 256

Multiaxial Impact

125

J

ISO 6603

Instrumented Impact Total Energy, 23°C

80

J

ASTM D 3763

Izod Impact, unnotched 80*10*3 +23°C

NB

kJ/m2

ISO 180/1U

Izod Impact, unnotched 80*10*3 -30°C

NB

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*3 +23°C

13

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

6

kJ/m2

ISO 180/1A

Izod Impact, unnotched 80*10*4 +23°C

NB

kJ/m2

ISO 180/1U

Izod Impact, unnotched 80*10*4 -30°C

NB

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*4 +23°C

12

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

10

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

13

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

5

kJ/m2

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m2

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m2

ISO 179/1eU

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

14

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm

10

kJ/m2

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm

NB

kJ/m2

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm

NB

kJ/m2

ISO 179/1eU

THERMAL

value

Unit

Standard

Vicat Softening Temp, Rate B/50

114

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

104

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

93

°C

ASTM D 648

CTE, -40°C to 40°C, flow

6.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

6.E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

6.E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

114

°C

ISO 306

Vicat Softening Temp, Rate B/120

115

°C

ISO 306

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm

105

°C

ISO 75/Bf

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

95

°C

ISO 75/Af

PHYSICAL

value

Unit

Standard

Specific Gravity

1.33

-

ASTM D 792

Mold Shrinkage, flow (5)

0.5 - 0.7

%

SABIC Method

Mold Shrinkage, xflow (5)

0.5 - 0.7

%

SABIC Method

Melt Flow Rate, 300°C/1.2 kgf

12

g/10 min

ASTM D 1238

Density

1.33

g/cm3

ISO 1183

Melt Volume Rate, MVR at 300°C/1.2 kg

10

cm3/10 min

ISO 1133

FLAME CHARACTERISTICS

value

Unit

Standard

Heat release, MAHRE, 50 kW/m2, 3 mm

<60

kW/m2

ISO 5660-1

Smoke density, DS-4, 50 kW/m2, 3mm

<150

-

ISO 5659-2

Smoke density, VOF4, 50 kW/m2, 3mm

<300

-

ISO 5659-2

Smoke toxicity, CITG (8 min), 50 kW/m2, 3 mm

0.1

-

ISO 5659-2

Fire Safety Hazard Level - Requirement set R6

HL3

-

EN EN 45545-2:2013