Property
|
Test Condition
|
Unit
|
Standard
|
guide value
|
|
|
d.a.m.
|
cond.
|
|
Rheological properties
|
|
C
|
Molding shrinkage, parallel
|
60x60x2; 290 °C / MT 80 °C; 600 bar
|
%
|
ISO 294-4
|
0.5
|
|
|
C
|
Molding shrinkage, transverse
|
60x60x2; 290 °C / MT 80 °C; 600 bar
|
%
|
ISO 294-4
|
1.1
|
|
|
|
Post- shrinkage, parallel
|
60x60x2; 120 °C; 4 h
|
%
|
ISO 294-4
|
0.1
|
|
|
|
Post- shrinkage, transverse
|
60x60x2; 120 °C; 4 h
|
%
|
ISO 294-4
|
0.1
|
|
Mechanical properties (23 °C/50 % r. h.)
|
|
C
|
Tensile modulus
|
1 mm/min
|
MPa
|
ISO 527-1,-2
|
9000
|
5700
|
|
C
|
Tensile Stress at break
|
5 mm/min
|
MPa
|
ISO 527-1,-2
|
160
|
110
|
|
C
|
Tensile Strain at break
|
5 mm/min
|
%
|
ISO 527-1,-2
|
3.0
|
6.0
|
|
C
|
Charpy impact strength
|
23 °C
|
kJ/m2
|
ISO 179-1eU
|
55
|
70
|
|
C
|
Charpy impact strength
|
-30 °C
|
kJ/m2
|
ISO 179-1eU
|
45
|
45
|
|
C
|
Charpy notched impact strength
|
23 °C
|
kJ/m2
|
ISO 179-1eA
|
10
|
11
|
|
C
|
Charpy notched impact strength
|
-30 °C
|
kJ/m2
|
ISO 179-1eA
|
< 10
|
< 10
|
|
|
Charpy notched impact strength
|
|
kJ/m2
|
ISO 179-1eA
|
< 10
|
< 10
|
|
|
Izod notched impact strength
|
-30 °C
|
kJ/m2
|
ISO 180-1A
|
< 10
|
< 10
|
|
|
Izod notched impact strength
|
-40 °C
|
kJ/m2
|
ISO 180-1A
|
< 10
|
< 10
|
|
|
Flexural modulus
|
2 mm/min
|
MPa
|
ISO 178-A
|
7100
|
4700
|
|
|
Flexural strength
|
2 mm/min
|
MPa
|
ISO 178-A
|
260
|
165
|
|
|
Flexural strain at flexural strength
|
2 mm/min
|
%
|
ISO 178-A
|
5.0
|
7.0
|
|
|
Flexural stress at 3.5 % strain
|
2 mm/min
|
MPa
|
ISO 178-A
|
230
|
140
|
Thermal properties
|
|
C
|
Melting temperature
|
10 °C/min
|
°C
|
ISO 11357-1,-3
|
263
|
|
|
C
|
Temperature of deflection under load
|
1.80 MPa
|
°C
|
ISO 75-1,-2
|
240
|
|
|
C
|
Temperature of deflection under load
|
0.45 MPa
|
°C
|
ISO 75-1,-2
|
>250
|
|
|
C
|
Temperature of deflection under load
|
8.00 MPa
|
°C
|
ISO 75-1,-2
|
115
|
|
|
|
Vicat softening temperature
|
50 N; 120 °C/h
|
°C
|
ISO 306
|
> 230
|
|
|
C
|
Coefficient of linear thermal expansion, parallel
|
23 to 55 °C
|
10-4/K
|
ISO 11359-1,-2
|
0.3
|
|
|
C
|
Coefficient of linear thermal expansion, transverse
|
23 to 55 °C
|
10-4/K
|
ISO 11359-1,-2
|
1.1
|
|
|
C
|
Burning behavior UL 94
|
1.5 mm
|
Class
|
UL 94
|
HB
|
|
|
C
|
Oxygen index
|
Method A
|
%
|
ISO 4589-2
|
23
|
|
|
|
Glow wire test (GWFI)
|
2.0 mm
|
°C
|
IEC 60695-2-12
|
650
|
|
|
C
|
Vicat softening temperature
|
50 N; 50 °C/h
|
°C
|
ISO 306
|
230
|
|
Electrical properties (23 °C/50 % r. h.)
|
|
C
|
Relative permittivity
|
100 Hz
|
-
|
IEC 60250
|
4.0
|
10
|
|
C
|
Relative permittivity
|
1 MHz
|
-
|
IEC 60250
|
4.0
|
4.0
|
|
C
|
Volume resistivity
|
|
Ohm·m
|
IEC 60093
|
1E13
|
1E10
|
|
C
|
Surface resistivity
|
|
Ohm
|
IEC 60093
|
1E14
|
1E12
|
|
C
|
Electric strength
|
1 mm
|
kV/mm
|
IEC 60243-1
|
40
|
35
|
|
C
|
Comparative tracking index CTI
|
Solution A
|
V
|
IEC 60112
|
400
|
|
|
|
Comparative tracking index CTI M
|
Solution B
|
Rating
|
IEC 60112
|
275 M
|
|
Other properties (23 °C)
|
|
C
|
Water absorption (Saturation value)
|
Water at 23 °C
|
%
|
ISO 62
|
6,0
|
|
|
C
|
Water absorption (Equilibrium value)
|
23 °C; 50 % RH
|
%
|
ISO 62
|
2,1
|
|
|
C
|
Density
|
|
kg/m3
|
ISO 1183
|
1320
|
|
Processing conditions for test specimens
|
|
C
|
Injection molding-Melt temperature
|
|
°C
|
ISO 294
|
290
|
|
|
C
|
Injection molding-Mold temperature
|
|
°C
|
ISO 294
|
80
|
|
Processing recommendations
|
|
|
Drying temperature dry air dryer
|
|
°C
|
-
|
80
|
|
|
|
Drying time dry air dryer
|
|
h
|
-
|
2-6
|
|
|
|
Residual moisture content
|
|
%
|
Acc. to Karl Fischer
|
0.03.0.12
|
|
|
|
Melt temperature (Tmin - Tmax)
|
|
°C
|
-
|
280-300
|
|
|
|
Mold temperature
|
|
°C
|
-
|
80-120
|