| 详细介绍：
产品描述
CYCOLOY PC/ABS C1200HF物性表
Cycoloy C1200HF resin是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,加工方式为:注射成型。
Cycoloy C1200HF resin的主要特性有: 阻燃/额定火焰 、耐冲击、耐热、柔软。
适合于汽车、器具和电气元件
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL机械性能
|
value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
|
57
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
|
5
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
|
150
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min
|
2270
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
|
88
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
|
2340
|
MPa
|
ASTM D 790
|
|
IMPACT
|
value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
|
587
|
J/m
|
ASTM D 256
|
|
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
|
480
|
J/m
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C
|
54
|
J
|
ASTM D 3763
|
|
Instrumented IMPACT Total Energy, -30°C / 装有测量仪表的落镖冲击Total Energy，-30°C
|
54
|
J
|
ASTM D 3763
|
|
THERMAL
|
value
|
Unit
|
Standard
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
|
129
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
|
112
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
130
|
°C
|
ISO 306
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
105
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
80
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
105
|
°C
|
UL 746B
|
|
PHYSICAL
|
value
|
Unit
|
Standard
|
|
Specific Gravity/比重
|
1.15
|
–
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率, 260°C/5.0 kgf
|
19
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL
|
value
|
Unit
|
Standard
|
|
Hot Wire Ignition {PLC) / 热丝引燃 {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS 火焰特性
|
value
|
Unit
|
Standard
|
|
UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3)
|
1.19
|
mm
|
UL 94
|
|
CSA (See File for complete listing)
|
LS88480
|
File No.
|
CSA LISTED
|
|
Parameter
|
|
Injection Molding
|
value
|
Unit
|
|
Drying Temperature / 干燥温度
|
105 – 110
|
°C
|
|
Drying Time / 干燥时间
|
3 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥时间（累积的）
|
8
|
hrs
|
|
Maximum Moisture Content / 最大含湿量
|
0.04
|
%
|
|
Melt Temperature / 熔体温度
|
275 – 300
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
275 – 300
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
260 – 300
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
255 – 295
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
250 – 290
|
°C
|
|
Mold Temperature / 模具温度
|
60 – 90
|
°C
|
|
Back Pressure / 背压
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺杆速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
|
30 – 80
|
%
|
|
Vent Depth / 排气孔深度
|
0.038 – 0.076
|
mm
|
世界之名化工公司 与中国客户的桥梁
相关说明：正规的渠道进货，可提供COA报告,MSDS,SGS环保报告,UL黄卡及物性加工参数，可开17%的增值税 所售物资均为原厂原包，同时我们热烈欢迎广大客户来公司进行监督考察。相关承诺：我们希望能够长期的与客户合作，所以不谋取暴利，权衡利益，互利共赢！
订购说明：货物送达后，请时间检查外包装，如发现物流过程中出现大量包装损坏及原料外漏的，请让物流人员出具证明并保存，并在24小时内与我司相关人员取得联系，我们会快速度解决问题。
产品价格时有波动.详情请致电.以销售人员报价为实准！
|
放大图片
暂无相关下载