| 详细介绍：
产品参数
LEXAN”由双酚A制造，为聚碳酸脂这高分子材料，具有优异的高透明和耐热温度，以及热可塑性树脂中最高的冲击强度，良好的成型性使得“LEXAN”用于汽车零组件、事务机器、家电产品、电子产品、电子零件、食品器具、医疗器材和通信设备之替代金属用品上，最佳的选择材料。
产品描述
LEXAN PC 950物性表
不透明，高黏度、优良的阻燃性。少烟、有毒气体排放量低。
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL机械性能
|
value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
|
55
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
|
90
|
%
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
|
91
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
|
2240
|
MPa
|
ASTM D 790
|
|
Hardness, Rockwell M / 硬度, 洛氏 M
|
70
|
–
|
ASTM D 785
|
|
Hardness, Rockwell R / 硬度, 洛氏 R
|
118
|
–
|
ASTM D 785
|
|
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
IMPACT
|
value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
|
3204
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
|
640
|
J/m
|
ASTM D 256
|
|
Tensile Impact, Type “S” / 拉伸冲击值, 类型 “S”
|
525
|
kJ/m2
|
ASTM D 1822
|
|
Falling Dart IMPACT / 落锤冲击 (D 3029), 23°C
|
169
|
J
|
ASTM D 3029
|
|
THERMAL
|
value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
151
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed / 热变形温度，0.45 MPa, 6.4 mm, 未退火
|
137
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度，1.82 MPa, 6.4 mm, 未退火
|
132
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 95°C, flow / 热膨胀系数，-40°C 到 95°C, 流动
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity / 导热系数
|
0.19
|
W/m-°C
|
ASTM C 177
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL
|
value
|
Unit
|
Standard
|
|
Specific Gravity/比重
|
1.21
|
–
|
ASTM D 792
|
|
Specific Volume/比容
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Density/密度
|
1.217
|
g/cm3
|
ASTM D 792
|
|
Water Absorption, 24 hours / 吸水率， 24小时
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 23C / 吸水率，平衡，23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 100°C / 吸水率，平衡，100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率, 300°C/1.2 kgf / 熔流率，300°C/1.2 kgf
|
7
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL
|
value
|
Unit
|
Standard
|
|
Volume Resistivity/体积电阻率
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 3.2 mm / 介电强度，空气中，3.2 mm
|
16.7
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 50/60 Hz / 相对介电常数，50/60 Hz
|
3.01
|
–
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz / 相对介电常数，1 MHz
|
2.96
|
–
|
ASTM D 150
|
|
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz
|
0.0009
|
–
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz / 耗散因素，1 MHz
|
0.01
|
–
|
ASTM D 150
|
|
Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition {PLC) / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS
|
value
|
Unit
|
Standard
|
|
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
|
1.47
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
|
2.99
|
mm
|
UL 94
|
|
CSA (See File for complete listing)
|
LS88480
|
File No.
|
CSA LISTED
|
|
UV-light, water exposure/immersion / 紫外线暴露，耐水/浸渍
|
F1
|
–
|
UL 746C
|
|
Parameter
|
|
Injection Molding
|
value
|
Unit
|
|
Drying Temperature / 干燥温度
|
120
|
°C
|
|
Drying Time / 干燥时间
|
3 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥时间（累积的）
|
48
|
hrs
|
|
Maximum Moisture Content / 最大含湿量
|
0.02
|
%
|
|
Melt Temperature / 熔体温度
|
310 – 330
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
305 – 325
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
310 – 330
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
300 – 320
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
290 – 310
|
°C
|
|
Mold Temperature / 模具温度
|
80 – 115
|
°C
|
|
Back Pressure / 背压
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺杆速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
|
40 – 60
|
%
|
|
Vent Depth / 排气孔深度
|
0.025 – 0.076
|
mm
|
相关说明：正规的渠道进货，可提供COA报告,MSDS,SGS环保报告,UL黄卡及物性加工参数，可开17%的增值税发票，所售物资均为代理供应，同时我们热烈欢迎广大客户来公司进行监督考察。
公司承诺：我们希望能够长期的与客户合作，绝不谋取暴利，权衡利益，互利共赢！
订购说明：货物送达后，请时间检查外包装，如发现物流过程中出现大量包装损坏及原料外漏的，请让物流人员出具证明并保存，并在24小时内与我司相关人员取得联系，我们会度解决问题。
产品价格时有波动 详情请致电以销售人员报价为实准！
|
放大图片
暂无相关下载