| 详细介绍：
产品参数
LEXAN”由双酚A制造，为聚碳酸脂这高分子材料，具有优异的高透明和耐热温度，以及热可塑性树脂中最高的冲击强度，良好的成型性使得“LEXAN”用于汽车零组件、事务机器、家电产品、电子产品、电子零件、食品器具、医疗器材和通信设备之替代金属用品上，最佳的选择材料。
产品描述
Lexan PC 945物性表
非填充，注射级,无氯，非溴UL – 94 V0,有各种不透明的颜色,适用范围广。
Lexan* 945 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in various opaque color options. Lexan 945 is a general purpose resin designed to meet the needs of various applications.
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL/机械性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
|
65
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
|
125
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 50 mm/min
|
2270
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
101
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
2340
|
MPa
|
ASTM D 790
|
|
IMPACT/冲击性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
801
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
|
73
|
J
|
ASTM D 3763
|
|
THERMAL/热性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
143
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
126
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Specific Gravity / 比重
|
1.19
|
–
|
ASTM D 792
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.6 – 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL/电气性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Arc Resistance, Tungsten / 耐电弧性 {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
value/值
|
Unit/单位
|
Standard/标准
|
|
UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)
|
0.8
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)
|
1.14
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
3.04
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm
|
875
|
°C
|
IEC 60695-2-13
|
|
Oxygen Index / 极限氧指数 (LOI)
|
35
|
%
|
ISO 4589
|
|
Parameter
|
|
Injection Molding/注塑参数
|
value/值
|
Unit/单位
|
|
Drying Temperature / 干燥温度
|
120
|
°C
|
|
Drying Time / 干燥时间
|
3 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥时间（累积的）
|
48
|
hrs
|
|
Maximum Moisture Content / 最大含湿量
|
0.02
|
%
|
|
Melt Temperature / 熔体温度
|
295 – 315
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
290 – 310
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
295 – 315
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
280 – 305
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
270 – 295
|
°C
|
|
Mold Temperature / 模具温度
|
70 – 95
|
°C
|
|
Back Pressure / 背压
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺杆速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
|
40 – 60
|
%
|
|
Vent Depth / 排气孔深度
|
0.025 – 0.076
|
mm
|
相关说明：正规的渠道进货，可提供COA报告,MSDS,SGS环保报告,UL黄卡及物性加工参数，可开17%的增值税发票，所售物资均为代理供应，同时我们热烈欢迎广大客户来公司进行监督考察。
公司承诺：我们希望能够长期的与客户合作，绝不谋取暴利，权衡利益，互利共赢！
订购说明：货物送达后，请时间检查外包装，如发现物流过程中出现大量包装损坏及原料外漏的，请让物流人员出具证明并保存，并在24小时内与我司相关人员取得联系，我们会度解决问题。
产品价格时有波动 详情请致电以销售人员报价为实准！
|
放大图片
暂无相关下载