TYPICAL PROPERTIES (1)
|
|
MECHANICAL/机械性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
|
68
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
|
130
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 50 mm/min
|
2370
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
97
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
2340
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 M
|
70
|
–
|
ASTM D 785
|
|
Hardness，Rockwell / 洛氏硬度 R
|
118
|
–
|
ASTM D 785
|
|
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
Tensile Stress, yield / 抗张程度,屈服, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
Tensile Stress, break / 抗张程度,断裂, 50 mm/min
|
70
|
MPa
|
ISO 527
|
|
Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min
|
110
|
%
|
ISO 527
|
|
Tensile Modulus / 拉伸模量, 1 mm/min
|
2350
|
MPa
|
ISO 527
|
|
Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min
|
90
|
MPa
|
ISO 178
|
|
Flexural Modulus / 挠曲模量, 2 mm/min
|
2300
|
MPa
|
ISO 178
|
|
IMPACT/冲击性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C
|
3204
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
801
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 (natural, tints)
|
801
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 (colors)
|
801
|
J/m
|
ASTM D 256
|
|
Tensile Impact Type / 拉伸冲击值，类型”S”
|
577
|
kJ/m2
|
ASTM D 1822
|
|
Falling Dart Impact / 落锤冲击 (D 3029), 23°C
|
169
|
J
|
ASTM D 3029
|
|
Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C
|
63
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 +23°C
|
NA
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 -30°C
|
NA
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C
|
12
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
Charpy Impact, notched /简支梁缺口冲击强度, 23°C
|
35
|
kJ/m2
|
ISO 179/2C
|
|
Charpy（简支梁缺口冲击强度） 23°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm
|
NA
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy（简支梁缺口冲击强度） -30°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm
|
NA
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL/热性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
154
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
132
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 95°C, flow（流动）
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
Specific Heat / 比热
|
1.25
|
J/g-°C
|
ASTM C 351
|
|
Thermal Conductivity / 导热系数
|
0.19
|
W/m-°C
|
ASTM C 177
|
|
Thermal Conductivity / 导热系数
|
0.2
|
W/m-°C
|
ISO 8302
|
|
CTE（线形膨胀系数）, 23°C to 80°C, flow（流动）
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
–
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 A/50
|
153
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
141
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120
|
142
|
°C
|
ISO 306
|
|
HDT（热变形温度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
136
|
°C
|
ISO 75/Be
|
|
HDT（热变形温度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
125
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Specific Gravity / 比重
|
1.2
|
–
|
ASTM D 792
|
|
Specific Volume / 比容
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Density / 密度
|
1.19
|
g/cm3
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
10.5
|
g/10 min
|
ASTM D 1238
|
|
Melt Volume Rate / 溶化体积流率, MVR at 300°C/1.2 kg
|
10
|
cm3/10 min
|
ISO 1133
|
|
OPTICAL/光学性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Light Transmission / 透光率
|
88
|
%
|
ASTM D 1003
|
|
Haze / 雾度
|
1
|
%
|
ASTM D 1003
|
|
Refractive Index / 折射指数
|
1.586
|
–
|
ASTM D 542
|
|
ELECTRICAL/电气性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Volume Resistivity / 体积电阻率
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air / 介电强度，空气中, 3.2 mm
|
14.9
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相对介电常数, 50/60 Hz
|
3.17
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相对介电常数, 1 MHz
|
2.96
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.0009
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.01
|
–
|
ASTM D 150
|
|
Hot Wire Ignition / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
Volume Resistivity / 体积电阻率
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity ROA / 表面电阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity / 相对介电常数, 50/60 Hz
|
2.7
|
–
|
IEC 60250
|
|
Relative Permittivity / 相对介电常数, 1 MHz
|
2.7
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.001
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.01
|
–
|
IEC 60250
|
|
FLAME CHARACTERISTICS/火焰特性
|
value/值
|
Unit/单位
|
Standard/标准
|
|
UL Recognized, 94HB Flame Class Rating / 阻燃等级 (3)
|
1.47
|
mm
|
UL 94
|
|
Oxygen Index / 极限氧指数 (LOI)
|
25
|
%
|
ASTM D 2863
|
|
Oxygen Index / 极限氧指数 (LOI)
|
25
|
%
|
ISO 4589
|
放大图片