LG ABS AF312C 物性表

基本信息 ?

特性?阻燃性?

用途?电气/电子应用领域?

加工方法?注射成型?

物理性能?额定值?单位制?测试方法?

比重?1.18?g/cm3?ASTM D792?

熔流率（熔体流动速率）?(220°C/10.0 kg)?58?g/10 min?ASTM D1238?

收缩率 - 流动?(3.20 mm)?0.40 到 0.70?%?ASTM D955?

硬度?额定值?单位制?测试方法?

洛氏硬度?(R 级)?104??ASTM D785?

机械性能?额定值?单位制?测试方法?

拉伸模量?1(3.20 mm)?2160?MPa?ASTM D638?

抗张强度?2(屈服, 3.20 mm)?45.1?MPa?ASTM D638?

伸长率?3???ASTM D638?

????屈服, 3.20 mm?5.0?%?ASTM D638?

????断裂, 3.20 mm?20?%?ASTM D638?

弯曲模量?4(6.40 mm)?2550?MPa?ASTM D790?

弯曲强度?5(屈服, 6.40 mm)?68.6?MPa?ASTM D790?

冲击性能?额定值?单位制?测试方法?

悬壁梁缺口冲击强度???ASTM D256?

????-30°C, 3.20 mm?78?J/m?ASTM D256?

????-30°C, 6.40 mm?78?J/m?ASTM D256?

????23°C, 3.20 mm?260?J/m?ASTM D256?

????23°C, 6.40 mm?230?J/m?ASTM D256?

热性能?额定值?单位制?测试方法?

载荷下热变形温度???ASTM D648?

????0.45 MPa, 未退火, 6.40 mm?6?84.0?°C?ASTM D648?

????0.45 MPa, 未退火, 6.40 mm?7?76.0?°C?ASTM D648?

维卡软化温度?84.0?°C?ASTM D1525?8?

RTI Elec?80.0?°C?UL 746?

RTI Imp?70.0?°C?UL 746?

RTI?80.0?°C?UL 746?

可燃性?额定值??测试方法?

UL 阻燃等级???UL 94?

????2.50 mm?V-0??UL 94?

????3.00 mm?V-0??UL 94?